PS Electronic Plastic Blister Packaging

 

Specifications
Blister packaging
- Vacuum formed Tray
- PVC, PS material
- Logo or name customized
- CAD drawing and 3D modeling

Plastic Blister Packaging
GENERAL INFORMATION                                                                                                 
Plastic blister packaging tray is made of PVC or PS as basic material. It can nomal or be made with antistatic or ESD properties with black color. It has very good property and the conductive property will not be influenced by any humidity and temperature factors. It is permanent conductive.
We could make quick customize design. 3D model and 2D drawing will be made for PVC Blister mold. Different mold could be selected with balance of Qty. and cost.
 
Material: PS
Thickness: 0.3-8.0mm
Appearance: Transparent or black
Customized: width and length, thickness as customer request
Conductive: 10e4-10e6 ohms
Anti-static: 10e9-10e11 ohms
Model: 3400
 
APPLICATION of Plastic Blister Packaging                        
Disk industries
Semiconductor industries
Electronic product assembly and packaging
 
This material can be made into IC tray, LCD tray, Electronic Component tray, FPC tray etc. The surface resistance is very stable even after vacuum forming. It has very good property and the conductive property will not be influenced by any humidity and temperature factors.

Plastic Blister PackagingTECHNICAL DATA

Property	Test Method	British System Value   Unit	Intl. System Value   Unit	Metric System Value   Unit
Basic Physical Property
Melt flow rate	ASTM D 1238	2.8   g/10 min	2.8   g/10 min	2.8   g/10 min
Proportion	ASTM D 792	1.05	1.05	1.05
Extrusion molding data Mechanical Property
Tensile Strength	ASTM D 638	2600       psi	18       Mpa	183     kg/cm2
Breaking Strength	ASTM D 638	2400       psi	17       Mpa	169     kg/cm2
Breaking Elongation	ASTM D 638	40         %	40         %	40         %
Tensile Modulus	ASTM D 790	230000     psi	1600     Mpa	16200   kg/cm2
Notch Impact Strength @23oC	ASTM D 256	1.4     ft-lb/in	75         J/m	8   kg-cm/cm
Thermal Property
Vicat Softening Point	ASTM D 1238	212         oF	100         oC	100       oC
Heat Distortion Temperature @1.8MPa	ASTM D 648	198         oF	92         oC	92       oC